生産工程：
成分---->混合---->押出/カレンダー加工/射出成形---->加工---->磁化---->検査---->梱包
|
Grade |
MT(G) |
KA/m (Oe) |
KA/m (Oe) |
KJ/m3(MGOe) |
|
PRM-5T |
140-155 (1400-1550) |
90-120 (1125-1500) |
130 (1625) |
4.0-5.6 (0.5-0.7) |
|
PRM-8 |
160-185 (1600-1850) |
120-140 (1500-1750) |
150 (1875) |
5.6-7.0 (0.7-0.89) |
|
PRM-10 |
200-210 (2000-2100) |
145 (1812) |
160 (2000) |
8.0-9.6 (1.0-1.20) |
|
PRM-11 |
230-245 (2300-2450) |
160 (2000) |
175 (2188) |
10.0-11.0 (1.25-1.39) |
|
PRM-13 |
250 (2500) |
160 (2000) |
182 (2275) |
11.2-12.6 (1.40-1.51) |
|
PRM-15 |
260 (2600) |
172 (2150) |
196 (2450) |
12.0-12.8 (1.50-1.60) |
|
PRM-11H |
230-240 (2300-2400) |
170 (2125) |
188 (2500) |
10.0-11.0 (1.25-1.34) |
Magnetic characteristic of rubber magnet
|
Classification |
Type |
MT（GS） |
Hcb KA/m (Oe) |
KA/m(Oe)
|
(BH)max KJ/ m3(MGOe) |
Composition |
Mode of production |
|
Isotropic Rubber Magnet |
YNT-4 |
135-155(1350-1550) |
85-105(1050-1300) |
175-210(2200-2600) |
3.2-5.0(0.40-0.62) |
BaO.6Fe2O3 SrO.6Fe2O3 |
Extruding Rolling |
|
YNT-S5 |
165-180 (1650-1800) |
90-105 (1130-1300) |
135-160(1700-2010) |
4.5-5.8(0.56-0.72) |
|||
|
YNT-B5 |
170-190 (1700-1900) |
90-115 (1200-1450 |
150-190(1885-2400) |
4.6-6.5(0.57-0.80) |
|||
|
YNT-6.5 |
185-200(1850-2000) |
90-110(1130-1380) |
125-150(1570-1885) |
6.0-7.0(0.74-0.93) |
|||
|
Anisotropic Rubber Magnet |
YNY-10 |
220-240(2200-2400) |
140-165(1760-2070) |
200-235(2500-2950) |
9.0-10.5(1.1-1.30) |
SrO.6Fe2O3
|
Rolling |
|
YNY-11 |
230-250(2300-2500) |
145-165(1820-2070) |
190-225 (2380-2850) |
9.5-11.0(1.18-1.36) |
|||
|
YNY-13 |
250-270(200-2700) |
175-190(2200-2400) |
200-230 (2500-2900) |
11.5-14.5(1.42-1.80) |
|||
|
YNY-15 |
≥270(≥2700) |
175-190(2200-2400) |
200-230(2500-2900) |
≥14.5(≥1.8) |
その他の身体的特徴
密度 ： 3.6-3.8 g/cm3
ショア硬度 ： 30-60 ショア D
温度係数 ： -0.2 %/ °C
使用温度： -40~80℃